Performance | Unit | SMC | Fiberglass Reinforced ABS | Steel | Aluminum |
Density | g/cm³ | 1.7~1.9 | 1.25~1.38 | 7.8~7.9 | 2.7~2.8 |
Fiberglass Content | % | 15~60 | 20~40 | ||
Flexural Strength | Mpa | 90~360 | 160~170 | 250~450 | 140~240 |
Flexural Modulus | Gpa | 8~20 | 310 | 210 | 60 |
Tensile Strength | Mpa | 50~230 | 75~110 | 250~450 | 100~200 |
Tensile Modulus | Gpa | 10~17 | 4~6 | 210 | 60 |
Remark | Item | Density | Water Absorbing Performance | Mould Plastic Shrinkage Rate | Fiberglass Content | Heat Deformation Temperature | Flexural Strength | Flexural Modulus | Punch Strength | Tensile Strength | Dielectric Strength |
General SMC | Standard | GB /T1463 | GB /T1462 | GB /T15568 | GB /T15568 | GB /T1634 | GB /T1449 | GB /T1449 | GB /T1451 | GB /T1447 | GB /T1408 |
Unit | g/cm3 | mg | % | % | ℃ | Mpa | Gpa | KJ/m² | Mpa | KV/mm | |
1028 | 1.75-1.85 | ≤20 | ≤0.15 | 21±2 | ≥200 | ≥130 | ≥9 | ≥45 | ≥50 | ||
1039 | 1.75-1.85 | ≤20 | ≤0.15 | 26±2 | ≥200 | ≥150 | ≥10 | ≥60 | ≥65 | ||
1040 | 1.75-1.85 | ≤20 | ≤0.10 | 26±2 | ≥200 | ≥150 | ≥10 | ≥55 | ≥60 | ||
1045 | 1.75-1.85 | ≤20 | ≤0.15 | 19±2 | ≥200 | ≥110 | ≥9 | ≥40 | ≥45 | ||
1045DC | 1.75-1.85 | ≤20 | ≤0.15 | 21±2 | ≥200 | ≥130 | ≥9 | ≥45 | ≥50 | ||
1046 | 1.75-1.85 | ≤20 | ≤0.15 | 26±2 | ≥200 | ≥150 | ≥10 | ≥60 | ≥65 | ||
1046A | 1.75-1.85 | ≤20 | ≤0.12 | 32±2 | ≥200 | ≥170 | ≥10 | ≥65 | ≥70 | ||
1081 | 1.75-1.85 | ≤20 | ≤0.12 | 28±2 | ≥200 | ≥160 | ≥10 | ≥65 | ≥70 | ||
1081R | 1.75-1.85 | ≤20 | ≤0.12 | 30±2 | ≥200 | ≥170 | ≥10 | ≥75 | ≥80 | ||
1081TX | 1.80-1.90 | ≤20 | ≤0.10 | 36±2 | ≥200 | ≥190 | ≥11 | ≥85 | ≥90 | ||
1086 | 1.80-1.90 | ≤20 | ≤0.10 | 38±2 | ≥200 | ≥200 | ≥11 | ≥95 | ≥100 | ||
Low Shrinkage SMC | 1036 | 1.75-1.85 | ≤20 | ≤0.05 | 23±2 | ≥200 | ≥130 | ≥8 | ≥40 | ≥45 | |
1037 | 1.75-1.85 | ≤20 | ≤0.05 | 28±2 | ≥200 | ≥170 | ≥10 | ≥75 | ≥85 | ||
1080 | 1.75-1.85 | ≤20 | ≤0.05 | 30±2 | ≥200 | ≥150 | ≥9 | ≥70 | ≥70 | ||
1082 | 1.75-1.85 | ≤20 | ≤0.08 | 28±2 | ≥200 | ≥170 | ≥10 | ≥80 | ≥80 | ||
1083 | 1.75-1.85 | ≤20 | ≤0.08 | 28±2 | ≥200 | ≥170 | ≥10 | ≥80 | ≥80 | ||
Flame Retardant SMC | 2010 | 1.75-1.85 | ≤20 | ≤0.15 | 23±2 | ≥200 | ≥140 | ≥9 | ≥50 | ≥50 | ≥12 |
2017 | 1.75-1.85 | ≤20 | ≤0.10 | 28±2 | ≥200 | ≥170 | ≥10 | ≥70 | ≥70 | ≥12 | |
2039 | 1.75-1.85 | ≤20 | ≤0.15 | 23±2 | ≥200 | ≥140 | ≥9 | ≥50 | ≥50 | ≥10 | |
2045 | 1.75-1.85 | ≤20 | ≤0.15 | 20±2 | ≥200 | ≥110 | ≥9 | ≥45 | ≥45 | ≥10 | |
2050 | 1.75-1.85 | ≤20 | ≤0.15 | 24±2 | ≥200 | ≥140 | ≥9 | ≥50 | ≥55 | ≥12 | |
2070 | 1.75-1.85 | ≤20 | ≤0.15 | 26±2 | ≥200 | ≥150 | ≥10 | ≥60 | ≥65 | ≥12 | |
2076 | 1.75-1.85 | ≤20 | ≤0.15 | 26±2 | ≥200 | ≥150 | ≥10 | ≥60 | ≥65 | ≥10 | |
2082 | 1.80-1.90 | ≤20 | ≤0.08 | 36±2 | ≥200 | ≥180 | ≥11 | ≥85 | ≥85 | ≥12 | |
2082T | 1.80-1.90 | ≤20 | ≤0.05 | 33±2 | ≥200 | ≥180 | ≥11 | ≥90 | ≥95 | ≥12 | |
2088 | 1.80-1.90 | ≤20 | ≤0.08 | 36±2 | ≥200 | ≥180 | ≥11 | ≥85 | ≥85 | ≥12 |
Remark | Insulation Resistance | Electric Resistance Arc | Dielectric Coefficient | Electric Loss (TAN) | Electric Leakage Resttance Crease Index | Combustion Resistance | Notes |
General SMC | G B/T10064 | GB /T1411 | GB /T1409 | GB /T1409 | GB /T4207 | UL-94 | |
Ω | S | V | Grade | ||||
The surface effect is general,suitable for ordinary products | |||||||
Good surface effect, general purpose | |||||||
Class A surface finish, suitable for bathroom products | |||||||
The surface effect is average, suitable for ordinary products | |||||||
Good surface effect, suitable for watch box products | |||||||
Slightly lower strength, suitable for ordinary products in the automotive industry | |||||||
Good surface effect,high strength, good water resistance, suitable for large water tank products | |||||||
High strength, suitable for the automotive industry | |||||||
High strength, good surface effect, suitable for colored exterior parts such as cars | |||||||
High strength, suitable for large products in automotive and other fields | |||||||
High strength, general surface effect, suitable for high-strength and high-frequency vibrationparts of construction machinery | |||||||
Low Shrinkage SMC | Class A surface effect, suitable for bathroom and high surface effect flat panel | ||||||
Class A surface effect, high strength, suitable for the automotive industry | |||||||
Class A surface effect, high strength, suitable for the automotive industry | |||||||
High strength, with certain anti-corrosion properties | |||||||
High strength, good corrosion resistance | |||||||
Flame Retardant SMC | ≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V0 | General surface effect, general purpose |
≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V0 | Strength, suitable for bracket products in railway industry | |
≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V1 | General flame retardancy, suitable for insulating boards | |
≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V1 | General surface effect, general purpose | |
≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V0 | Good surface effect, suitable for watch box products | |
≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V0 | Fortunately, the light transmittance is suitable for medical CT cover | |
≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V1 | Good surface effect, suitable for watch box products | |
≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V0 | High strength, suitable for subway seats and other load-bearing products | |
≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V0 | A-arade surface effect, high strenath, suitaple for high-speed rail subway wall panel products.meet the standards of the Ministry of Railwavs, HL2 standards in EN45545. etc. | |
≥1.0×1013 | ≥180 | ≤4.5 | ≤0.015 | ≤600 | V0 | High strength, suitable for railway cable ducts |
Welcome to TIANMA, a leading provider of high-quality SMC (Sheet Moulding Compounds) and BMC (Bulk Moulding Compounds) molded materials. At TIANMA, we specialize in delivering top-notch solutions for a wide range of applications, ensuring superior performance and reliability in every project.
SMC Compound: Engineered ExcellenceOur SMC compounds are meticulously formulated to meet the most demanding engineering requirements. These versatile materials, often referred to as "smc compound" or "smc sheet moulding compounds," exhibit exceptional strength, impact resistance, and dimensional stability. TIANMA's SMC compounds find applications in diverse industries, including automotive, aerospace, and electrical, where their unique combination of properties ensures optimal performance and longevity.
SMC Sheet Moulding Compounds: Tailored for SuccessTIANMA takes pride in offering a comprehensive range of "smc sheet moulding compounds" designed to cater to specific manufacturing needs. These compounds are characterized by their excellent flow characteristics, allowing for intricate mold filling and precise replication of details. From automotive body panels to electrical enclosures, our SMC sheet moulding compounds play a crucial role in enhancing product aesthetics, durability, and overall functionality.
SMC Molded Material: Unleashing InnovationExperience innovation like never before with TIANMA's SMC molded materials. Renowned for their adaptability and reliability, our "smc molded material" solutions empower manufacturers to create complex and intricate components with ease. Whether you're developing lightweight structural parts or corrosion-resistant components, TIANMA's SMC molded materials offer a winning combination of performance and cost-effectiveness.
BMC Molded Material: Precision RedefinedIn addition to SMC, TIANMA excels in providing high-quality BMC molded materials. These materials, often known as "bmc molded material," are tailored for applications where intricate shapes and tight tolerances are essential. With excellent electrical insulation properties and flame resistance, our BMC molded materials are the preferred choice for electrical and electronic applications, ensuring safety and reliability.
Choose TIANMA for Your Molding SolutionsTIANMA stands as your reliable partner in delivering cutting-edge SMC/BMC molded materials. Our commitment to quality, innovation, and customer satisfaction sets us apart in the industry. Explore the possibilities with TIANMA and elevate your projects with our exceptional "smc compound," "smc sheet moulding compounds," and "smc molded material" solutions.
Rail transportation
Decorative Materials
Toilet Utensils
Other Materials
Tianma Group Corp is engaged in research on fiberglass/composite material products and related technologies, and has won multiple national, provincial, and municipal level scientific and technological progress awards. Based on this, the company implements a technological innovation strategy, actively cooperates with domestic and foreign research institutes, targets and tracks international market trends, continuously develops new products with independent intellectual property rights, and enhances core competitiveness.
E-mail: sales1@tm253.com
Tel: 0086-519-68193652
Add: No. 309 Huanghai Rd, Xinbei District, Changzhou, Jiangsu, China